New Aluminum Brazing Rod.

Old 05-08-07, 10:56 AM
  #1  
Faith-Vigilance-Service
Thread Starter
 
Patriot's Avatar
 
Join Date: Jul 2004
Location: Port Orchard, WA
Posts: 8,330

Bikes: Trinity, Paradisus, Centurion, Mongoose, Trek

Mentioned: 1 Post(s)
Tagged: 0 Thread(s)
Quoted: 0 Post(s)
Likes: 0
Liked 1 Time in 1 Post
New Aluminum Brazing Rod.

HTS-2000.

Have you guys heard of this stuiff?

If you had the latest in alloy brazing rod technology available to repair that old 7005 aluminum bike frame, a brazing rod that is actually stronger that the original tig welding, would you use it? It's not Alumaweld, or any of the other commonly known rods. From what understand, it's relatively new. I couldn't help but scratch my head at the properties of this stuff.

Now, I'm no welding expert, so I thought I would post this here to see what the welders on here had to say or comment on this.

PHYSICAL PROPERTIES

Tensile: 45,900 PSI
Therm. Exp.: 15.2 x 10- 6in./in./F°
Elongation: 10% in 2 inches
Elec. Cond: 26 (% of copper std.)
Impact: 43 Ft. lbs (charpy)
S.P. Grav.: 6.6
Shear: 31,000 PSI
Weight: 0.24 lbs/cu. in.
Melting Point: 717°- 737°
Rockwell: 48

Here's the video they show.

https://aluminumrepair.com/login/Vide.../newflash.html

I have an old aluminum frame I'd like to repair, and when I saw this online demo video, I couldn't help but ask a friend of mine who welds aluminum. He heard of it too, but never saw it use dbefore, as it hasn't been out for long. If this stuff is no B.S., then alloy repairs will become an everyday acceptance.
__________________
President, OCP
--"Will you have some tea... at the theatre with me?"--
Patriot is offline  
Old 05-09-07, 11:56 AM
  #2  
Senior Member
 
DannoXYZ's Avatar
 
Join Date: Jul 2005
Location: Saratoga, CA
Posts: 11,736
Mentioned: 1 Post(s)
Tagged: 0 Thread(s)
Quoted: 109 Post(s)
Liked 9 Times in 6 Posts
That look pretty promising! I've actually had good luck with the Alumaweld rods. But only on 6061 alloys. The zinc content of 7005 makes it difficult to stick. You should ask them if this HTS stuff actually works on 7005. I also suspect like steel-brazing that it doesn't like big gaps to be bridged. The parts should fit as precisely as possible.
DannoXYZ is offline  
Old 05-09-07, 01:48 PM
  #3  
Faith-Vigilance-Service
Thread Starter
 
Patriot's Avatar
 
Join Date: Jul 2004
Location: Port Orchard, WA
Posts: 8,330

Bikes: Trinity, Paradisus, Centurion, Mongoose, Trek

Mentioned: 1 Post(s)
Tagged: 0 Thread(s)
Quoted: 0 Post(s)
Likes: 0
Liked 1 Time in 1 Post
I have an old Rockhopper I am rebuilding, and I found a crack that goes about halfway around the tubing on one of the chainstays, about 2" behind the BB shell. It look slike the chain came off and jammed in there and damaged the tube, causing it to crack. It's just a hairline crack that goes about 50% around the tube.

Well, I do know that when repairing aluminum with this brazing rod, they show a butt weld as the process. They show how a crack is basically "V'd" out so the braze can fill it in. They also said that with Aluminum, the "tinning" is really a necessary part. I would think the more you really scrub the surface with the molten rod and a SS brush, it will penetrate and stick better. Not sure though.

If I can't find someone to do a really good TIG weld to fix it, then I may just give it a shot, as I have nothing to lose at that point.
__________________
President, OCP
--"Will you have some tea... at the theatre with me?"--
Patriot is offline  
Old 05-11-07, 03:24 PM
  #4  
Senior Member
 
DannoXYZ's Avatar
 
Join Date: Jul 2005
Location: Saratoga, CA
Posts: 11,736
Mentioned: 1 Post(s)
Tagged: 0 Thread(s)
Quoted: 109 Post(s)
Liked 9 Times in 6 Posts
Be very careful with the torch! Aluminium doesn't glow when heated and you might get it hotter than the melting-temp of the underlying alloy. Best to keep the torch and the rod moving quickly like they have on the the video; just enough heat to flow the brazing-rod. I've actually successfully replaced a dropout on a Cannondale with the Alumaweld brazing rods.
DannoXYZ is offline  
Old 05-11-07, 09:51 PM
  #5  
Faith-Vigilance-Service
Thread Starter
 
Patriot's Avatar
 
Join Date: Jul 2004
Location: Port Orchard, WA
Posts: 8,330

Bikes: Trinity, Paradisus, Centurion, Mongoose, Trek

Mentioned: 1 Post(s)
Tagged: 0 Thread(s)
Quoted: 0 Post(s)
Likes: 0
Liked 1 Time in 1 Post
^^^ That's exactly what the manufacturer told me. Keep the torch moving. When it melts, keep it on for just a couple seconds more, because it takes a few more degrees for the rod to penetrate and stick to the aluminum. We went trhough the tinning process and so forth, so I'm gonna give it a shot. Apparently, the tinning is the key to getting it to work on aluminum for best results. It needs a good scrubbing when the rod is wet.

I have an air-acetylene "turbo torch" at work which I will be using. It has a good wide flame to cover a good area to prevent concentrated heat from burning a hole. I also have a bunch of scrap aluminum flat stock to practice with.
__________________
President, OCP
--"Will you have some tea... at the theatre with me?"--
Patriot is offline  
Old 05-12-07, 12:46 AM
  #6  
Senior Member
 
bellweatherman's Avatar
 
Join Date: Aug 2005
Location: Austin
Posts: 2,104

Bikes: Too many to count

Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Likes: 0
Liked 1 Time in 1 Post
I don't think anybody has actually tried to braze an entire aluminum frame.
bellweatherman is offline  
Old 04-10-09, 10:11 PM
  #7  
Senior Member
 
Join Date: Apr 2009
Posts: 142
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 0 Post(s)
Likes: 0
Liked 0 Times in 0 Posts
Originally Posted by bellweatherman
I don't think anybody has actually tried to braze an entire aluminum frame.
Why have you formed this opinion?
KonaBuyer is offline  
Old 04-11-09, 07:59 AM
  #8  
Randomhead
 
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,364
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,664 Times in 2,497 Posts
I have heard that there is no point to any of this if you can't heat treat the whole thing after you are done. Annealed aluminum has the mechanical properties of a warm chocolate bar.
unterhausen is offline  
Old 04-11-09, 09:16 AM
  #9  
Uber Goober
 
StephenH's Avatar
 
Join Date: Sep 2007
Location: Dallas area, Texas
Posts: 11,758
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 190 Post(s)
Liked 41 Times in 32 Posts
That's what I was wondering about, too. If the frame in question was heat-treated after welding, then you'd lose a lot of the strength if you welded or brazed it without heat treating it again. But I don't know how common that actually is on bikes. Some research into the alloys should show you if they're heat treatable.
__________________
"be careful this rando stuff is addictive and dan's the 'pusher'."
StephenH is offline  
Old 04-11-09, 05:43 PM
  #10  
Senior Member
 
PaPa's Avatar
 
Join Date: May 2003
Location: Idaho
Posts: 496
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 1 Post(s)
Likes: 0
Liked 0 Times in 0 Posts
If the frame was originally 6061-T6, then it has a tensile of about 42,000 psi. After welding you can expect to lose over half, or about 18,000 psi in the HAZ. It's risky business to repair thin aluminum tubes then bypass proper post heat treatment. I would not use HTS-2000 for anything structural. However it's fine for patching holes in aluminum boat hulls or sprinkler pipes.
PaPa is offline  
Old 04-11-09, 08:47 PM
  #11  
deep stuff
 
brucewiley's Avatar
 
Join Date: Jun 2007
Location: Nampa, ID
Posts: 250

Bikes: Road, Touring, Mountain Bike

Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 0 Post(s)
Likes: 0
Liked 0 Times in 0 Posts
Originally Posted by PaPa
If the frame was originally 6061-T6, then it has a tensile of about 42,000 psi. After welding you can expect to lose over half, or about 18,000 psi in the HAZ.
I'm curious now. Is there really an HAZ to treat if you are brazing and not melting (welding) the base aluminum metal, similar to brazing steel. Is there an HAZ with the brass in the case of steel that needs to be heat treated? I don't think so in most cases.

I'm just an old welder and not a metallurgist but doesn't 6061 T6 regain it's strength through aging and not heat treatment? (maybe not including an HAZ as in the case of TIG)

Enlighten me.

Bruce
brucewiley is offline  
Old 04-12-09, 08:58 PM
  #12  
Banned
 
Join Date: Aug 2005
Posts: 5,115
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 0 Post(s)
Likes: 0
Liked 2 Times in 1 Post
"Is there an HAZ with the brass in the case of steel that needs to be heat treated? I don't think so in most cases."

Not if the metal wasn't heat treated for hardness in the first place, or unless the welding caused the metal to harden. If you are just welding normal structural steel, or chromo aircraft tubing then you don't need to heat treat. If you are brazing a metal that was heat treated, then you may, it would depend on whether the extra properties are actually required where you brazed, for instance if you brazed a butt, and didn't affect the thin waleld section of the tube. Same goes for inducing hardness in metal, if it isn't to a negative degree as it won't tend to be in low carbon steel, then localized differences may not mater.

Aluminum is not something I really understand where heat treating is concerned. I have heard other stories of a readjustment over time, but if it was that simple why would they bother heat treating frames. I thinkt he big issue is with 7075-t6

Last edited by NoReg; 04-12-09 at 09:02 PM.
NoReg is offline  
Old 04-12-09, 09:16 PM
  #13  
Randomhead
 
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,364
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,664 Times in 2,497 Posts
Of course there is a HAZ. Annealed 6061 is not something you would want to use on a bike in a part that carries stress.
unterhausen is offline  
Old 04-12-09, 09:58 PM
  #14  
Senior Member
 
PaPa's Avatar
 
Join Date: May 2003
Location: Idaho
Posts: 496
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 1 Post(s)
Likes: 0
Liked 0 Times in 0 Posts
Originally Posted by brucewiley
I'm curious now. Is there really an HAZ to treat if you are brazing and not melting (welding)
HAZ (or Heat Affected Zone) is determined by temperature, not jointing method. Partial annealing (reduction in tensile) begins when temperature of almost any tempered aluminum alloy reaches between 350f and 400f. Full annealing occurs at 500f to 700f. Liquidus (welding) is about 1200f.

Originally Posted by brucewiley
Is there an HAZ with the brass in the case of steel that needs to be heat treated?
Generally speaking, steel has a much higher tensile than most aluminum alloys to begin with, so any tensile loss due to annealing is largely insignificant.

Originally Posted by brucewiley
I'm just an old welder and not a metallurgist but doesn't 6061 T6 regain it's strength through aging
Yes, usually. But you'll only achieve T4 - and will not happen overnight.
PaPa is offline  
Old 04-12-09, 10:35 PM
  #15  
Insane Bicycle Mechanic
 
Jeff Wills's Avatar
 
Join Date: Mar 2008
Location: other Vancouver
Posts: 9,811
Mentioned: 34 Post(s)
Tagged: 0 Thread(s)
Quoted: 788 Post(s)
Liked 688 Times in 367 Posts
Originally Posted by unterhausen
I have heard that there is no point to any of this if you can't heat treat the whole thing after you are done. Annealed aluminum has the mechanical properties of a warm chocolate bar.
Well... I heard that Roger Durham (of Bullseye pulley fame) built several oversize aluminum bike frames in the '70's. They lasted thousands of miles without incident, even though they weren't heat-treated post-welding. This came up in the Cannondale-Klein patent fight.
__________________
Jeff Wills

Comcast nuked my web page. It will return soon..
Jeff Wills is offline  
Old 04-12-09, 11:16 PM
  #16  
Senior Member
 
PaPa's Avatar
 
Join Date: May 2003
Location: Idaho
Posts: 496
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 1 Post(s)
Likes: 0
Liked 0 Times in 0 Posts
Originally Posted by Jeff Wills
Well... I heard that Roger Durham (of Bullseye pulley fame) built several oversize aluminum bike frames in the '70's. They lasted thousands of miles without incident, even though they weren't heat-treated post-welding.
I'd be interested in your references.

IIRC Roger was mechanical engineer and prone to careful structural analysis prior to melting tubes. His forte (among bolt-on bits'n pieces), was short and compact BMX and folders.
PaPa is offline  
Old 04-13-09, 12:34 AM
  #17  
Randomhead
 
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,364
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,664 Times in 2,497 Posts
I don't remember the details of the Bullseye bikes. Just because they lasted does not mean that a bike that was designed with the strength properties offered by heat treating will last after local annealing. And the frame in the OP has already demonstrated that it is marginal strength-wise. I'm sure the heat treating is a large expense that would be eagerly skipped if that was possible.
unterhausen is offline  
Old 04-13-09, 01:51 AM
  #18  
Senior Member
 
PaPa's Avatar
 
Join Date: May 2003
Location: Idaho
Posts: 496
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 1 Post(s)
Likes: 0
Liked 0 Times in 0 Posts
Two more tid-bits to ponder:

While HTS-2000 claims 45,900 PSI tensile, they are referring to bead strength... which is not to be confused with overall joint integrity after you've annealed it with heat. Use a flame, i.e. O/A, propane, Mapp, and you expand the HAZ, annealing even more tubing. Use TIG (GTAW), and the HAZ will be greatly reduced.

Most aluminum fractures I've seen occurred in the HAZ... just like this one
PaPa is offline  

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off
Trackbacks are Off
Pingbacks are Off
Refbacks are Off


Thread Tools
Search this Thread

Contact Us - Archive - Advertising - Cookie Policy - Privacy Statement - Terms of Service -

Copyright © 2024 MH Sub I, LLC dba Internet Brands. All rights reserved. Use of this site indicates your consent to the Terms of Use.