Bad idea. Ti is not as strong per cross sectional area as steel, so a part designed to be made from steel but then Ti is swapped in will result in a significantly weaker part. If you are a very lightweight person then it might be OK, but for the absolute minimal improvement it's not worth the trouble - any trouble.