i suspect that the crystal structure of the particular Mg alloy would be different from that of pure Mg
Probably not considering the frames are probably made from AZ61 which will only have ~7% alloying additions. It's also not a homogenous alloy either.
I have my ASM handbook in front of me so I'm not pulling this information out of my ass.