just monitor for cracks, it's not going to let go all at once. I'm not an expert, but it seems the bluing means that it was exposed to air while hot. I wonder if they cheapened out on the post-weld purge? The roughness is penetration. I think I would be a little more worried that they didn't weld the whole dt/ht interface.