Originally Posted by icemilkcoffee

Just like with any boat hull or any other composite object: use a hard object to tap along the carbon top tube. It should have a hard crisp knock to it. When you get to that chipped section, does the tone change? If there is no change in tone then I would say it's totally fine. If it turns into a thud then there is de-lamination.