Originally Posted by
unterhausen
I never had trouble with it on steel either. Why they used nickel silver on steel will forever be a mystery though. I suppose it could have been because it was stronger, not that it really matters.
When I asked, I was told that it fills large voids (like stay ends) better than low-fuming bronze.